학술지 Characteristics of Temperature and Wavelength Dependence of CuInSe2 Thin-Film Solar Cell with Sputtered Zn(O,S) and CdS Buffer Layers
Cited 18 time in scopus Download 5 time Share share facebook twitter linkedin kakaostory
위재형, 이우정, 조대형, 한원석, 윤재호, 정용덕
Physica Status Solidi (A), v.211 no.9, pp.2172-2176
Wiley-VCH Verlag GmbH
The sputtered-Zn(O,S) and -CdS films were prepared as a buffer layer in CuInSe2 (CIS) in the bottom cell of a Cu(In,Ga)Se2 (CIGS)-tandem-structured solar cell. We characterized the thermal stability and long wavelength response of the CIS solar cell. The thermal stability of CIS solar cell is tested in increasing annealing temperature up to 500 C in a vacuum for 60 min. The optical response of CIS solar cell was measured by using long-wavelength pass filter to verify availability as a bottom cell. The power conversion efficiency (PCE) of the sputtered-Zn(O,S)/CIS cell showed a slight drop from 9.73% as-fabricated to 9.61% after 60 min of annealing at 300 C, whereas the 7.97% as-fabricated PCE of the sputtered-CdS/CIS cell fully deteriorated above 300 C at 60 min of annealing. The PCE of as-fabricated-Zn(O,S)/CIS was 5.46% by using the selective 715 nm long-pass filter. This value remains almost unchanged after post-annealing, whereas the 4.36% PCE of as-fabricated-CdS/CIS solar cell by using the 715 nm long-pass filter continuously dropped after 60 min of 300 C annealing. The high-temperature-stability of the Zn(O,S) buffer was attributed to the smaller diffusivity of Zn atoms than that of Cd atoms.
CuInSe 2, long-pass filter, sputtered-CdS, sputtered-Zn(O S), thermal stability