ETRI-Knowledge Sharing Plaform

ENGLISH

성과물

논문 검색
구분 SCI
연도 ~ 키워드

상세정보

학술지 Effects of Controlling Cu Spacer Inter-Diffusion by Diffusion Barriers on the Magnetic and Electrical Stability of GMR Spin-Valve Devices
Cited 9 time in scopus Download 0 time Share share facebook twitter linkedin kakaostory
저자
Jing Jiang, Ding Gui Zeng, 류호준, Kyung-Won Chung, Seongtae Bae
발행일
201007
출처
Journal of Magnetism and Magnetic Materials, v.322 no.13, pp.1834-1840
ISSN
0304-8853
출판사
Elsevier
DOI
https://dx.doi.org/10.1016/j.jmmm.2009.12.036
초록
An ultra-thin Co or CoFe diffusion barrier inserted at the NiFe/Cu interfaces was revealed to effectively control the electrical and magnetic stability of NiFe/Cu/NiFe-based giant magnetoresistance (GMR) spin-valve spintronics devices (SVSDs) operating at high current density. It was found that the activation energy, Ea, related to the electromigration (EM)-induced inter-diffusion process for the patterned NiFe(3)/Cu(2)/NiFe(3 nm) magnetic multi-layered devices (MMLD) was remarkably increased from 0.52짹0.2 eV to 1.17짹0.16 eV after the insertion of an ultra-thin Co diffusion barrier at the NiFe/Cu interfaces. The dramatically reduced "current shunting paths" from the Cu spacer to the NiFe thin films and the development of "self-healing process" resulted from the effectively restrained Cu inter-diffusion (intermixing with Ni atoms) due to the diffusion barriers were found to be primarily responsible for the improvement of electrical and magnetic stability. The further investigation on the effects of controlling Cu spacer inter-diffusion by diffusion barriers on the EM and thermomigration (TM)-induced magnetic degradation was carried out for the NiFe/(Co or Co90Fe10)/Cu/(Co or Co90Fe10)/NiFe/FeMn top exchange-biased GMR (EBGMR) SVSDs electrically stressed under the applied DC current density of J=2.5×107 A/cm2 (I=16.5~17.25 mA). It was clearly confirmed that the Co and the CoFe diffusion barriers effectively control the Cu spacer inter-diffusion resulting in a smaller reduction in both GMR ratio and exchange bias field of the EBGMR SVSDs. Furthermore, it was obviously observed that the effects of CoFe diffusion barrier on controlling the Cu spacer inter-diffusion are more significant than that of Co. The effectively reduced Mn atomic inter-diffusion at the NiFe/FeMn interface and the well-maintained interfacial spin-dependent scattering resulted from the control of EM and TM-induced Cu spacer inter-diffusion were the main physical reasons for the significant improvement of magnetic and electrical degradation of top EBGMR SVSDs. © 2009 Elsevier B.V. All rights reserved.
키워드
Co and CoFe diffusion barrier, Controlling of Cu spacer inter-diffusion, Electrical and magnetic stability, GMR Spin-valve device