학술대회 Control of Na Diffusion from Soda-Lime Glass and NaF Film into Cu(In,Ga)Se2 for Thin-Film Solar Cells
Cited 1 time in scopus Download 0 time Share share facebook twitter linkedin kakaostory
저자
조대형, 정용덕, 이규석, 김주희, 박수정, 김제하
발행일
201206
출처
Photovoltaic Specialists Conference (PVSC) 2012, pp.1-4
DOI
https://dx.doi.org/10.1109/PVSC-Vol2.2013.6656704
협약과제
11FB1300, 초경량 CIGS 박막 태양전지 공정 기술 개발, 정용덕
초록
We report on the effect of Na incorporation into Cu(In,Ga)Se2 (CIGS) for thin-film solar cells. Na ions were supplied by NaF films with different thicknesses, while those from the soda-lime glass substrate were controlled by a presence or an absence of a SiOx barrier. Gradually increasing a Na content in CIGS was found in the structures of CIGS/Mo/SiO x/SLG, CIGS/Mo/SLG, CIGS/5 nm-NaF/Mo/SiOx/SLG, CIGS/5 nm-NaF/Mo/SLG, CIGS/15 nm-NaF/Mo/SiOx/SLG, and CIGS/15 nm-NaF/Mo/SLG. With increasing the Na content, the CIGS (112) preferential orientation growth became dominant, while the (220/204) one was nearly constant. The grain size decreased with increasing the Na content. The cell efficiency (η) increased for relatively low Na content however the thick NaF led to a degradation of η because of poor adhesion between the CIGS and the Mo. The sample with the CIGS/5 nm-NaF/Mo/SiOx/SLG structure achieved the comparable (112)/(220/204) peak ratios, grain sizes, as well as the cell performances to a CIGS/Mo/SLG structure that contains the same Na content in the CIGS. © 2012 IEEE.